UE 55-0500/3 is a UV cell coating for the BMW Gen5 platform (project period 2018 - 2030). It is applied by hot spray at 40℃, target film thickness 110 µm (70-145 µm). Key performance includes 3000 VDC BOL/EOL dielectric strength, insulation resistance >100GΩ BOL/EOL, very high anti sagging ability, GT0 adhesion, lap-shear BOL/EOL >8MPa. It offers coolant resistance. Validated by EOL1 240h 40℃/100%RH, EOL2 climate cycle test 30 days. It is REACH/RoHS confirm, no toxic or CMR category 1 ingredients. Online recycling utilization rate up to 95%, easy laser decoating.

UE 55-5700/0 is a UV cell coating for the Volvo platform (project period From 2024). It is applied by hot spray at 50℃, target film thickness 110 µm (70-155 µm). Key performance includes 3500 VDC BOL/EOL dielectric strength, insulation resistance >100GΩ BOL/EOL, very high anti sagging ability, GT0 adhesion, lap-shear BOL/EOL >10MPa. Validated by EOL1 168h 40℃/100%RH. It is REACH/RoHS, no toxic or CMR category 1 ingredients. Online recycling utilization rate up to 95%, easy laser decoating.

This product is suitable for cooling plates, featuring a viscosity of 700~900 mPas and excellent anti-sagging ability. It meets the 5000VDC resistance requirement for BOL/EOL, while possessing coolant resistance, water resistance, and corrosion resistance. It achieves GT0 adhesion and has a shear strength of ＞10MPa for BOL/EOL, with a thermal conductivity of ≥0.4W/(m·k). The product can pass the EOL 1000-hour durability test under D85 (85℃/85%RH) conditions and EOL 2000-hour SST (Salt Spray Test), and its online recyclability rate reaches up to 95%.

UE 55-5550/0 is a UV cell coating for the BMW Gen6 cylindrical cells (project period 2024 - 2038). It is applied by DOD at 40℃, target film thickness 130 µm. Key performance includes insulation resistance >100GΩ BOL/EOL, very high anti sagging ability, GT0 adhesion, lap-shear BOL/EOL >8MPa. It offers coolant resistance. Validated by EOL1 240h 40℃/100%RH. It is REACH/RoHS confirm, no toxic or CMR category 1 ingredients. Suitable for Nickel/Steel substrates.

This product features laser-free pre-treatment, achieving up to 30% cost savings in production line investment. It has a viscosity of 500-800 mPas and very high anti-sagging ability, while maintaining 4500VDC resistance and insulation resistance exceeding 100 GΩ throughout BOL and EOL stages. With coolant resistance, it achieves GT0 adhesion grade and retains a shear strength of ＞8MPa for both BOL and EOL unlasered. The product passes the EOL 1000-hour durability test under D85 (85℃/85%RH) conditions, complies with REACH and RoHS regulations.

Our latest development of spray coating. Transparent blue to provide readability of QR codes throughout the coating material. Designed for and approved by PowerCo Germany, Volkswagen's cell producer. The product was tailored perfectly to their requirements and withstands up to 5000VDC in 130 micron DFT, 8MPa lap-shear BOL & EOL, 20MPa pull-off BOL & EOL as well as 24mm bending.

"Think Pink". Color request from German OEM. High-End product equipped with performances such as 5000VDC, thermal conductivity of 0.7W/(m·k), >10MPa lap-shear BOL & EOL and an electrical resistance of >1TOhm.

Transparent yellow on customer request which can pass 2000h 85/85, 10MPa lap-shear BOL & EOL, 4500VDC Hi-Pot, >10GOhm resistance and electrolyte resistance of 7 days @55℃, utilization rate while using online recycling up to 95%.

Our first generation of UV Ink, LED 395nm curable, developed to match Xaar printheads (GS 40 etc.). The material is yellowish tinted on customer request and fulfills 2000h 85/85 and an electrolyte resistance of 7 days @ 55℃. Can be applied in two layers wet-in-wet or wet-on-dry (LED). The material fulfills GB 38031/2025.

Our first generation of UV Ink, LED 395nm curable, developed to match Xaar printheads (GS 40 etc.). The material is bluish tinted and fulfills 2000h 85/85 and an electrolyte resistance of 7 days @ 55℃. Can be applied in two layers wet-in-wet or wet-on-dry (LED). The material fulfills GB 38031/2025.

Our first generation of UV Ink, LED 395nm curable, developed to match Xaar printheads (GS 40 etc.). The material is reddish tinted and fulfills 2000h 85/85 and an electrolyte resistance of 7 days @ 55℃. Can be applied in two layers wet-in-wet or wet-on-dry (LED). The material fulfills GB 38031/2025.

SE 30 is a 2C-High Solid Epoxy material. Still up to date by its performance such as 4000VDC Hi-Pot resistance. It is commonly used for plates and framing parts as well as spot repair material on UV materials.